8433 CRC Ag-Au-Pd-Pt_3
Type: Sample show more
ObjectId: 77788 ExternalId: 8433
Created: 9/9/2026 3:53:42 PM by B01) Akbarnejad Elaheh [elaheh.akbarnejad@rub.de]
Updated: 9/10/2026 12:11:43 AM by INF) Victor Dudarev [vic.dudarev@gmail.com]
Access: Public Sort Code (asc): 0
License: CC BY 4.0
Description: Annealing at 600°C
[no file attached]
: Ag-Au-Pd-Pt
Associated Objects
-
Coupon
Substratepre sharpened microtips, APT
-
4NM_HEA_5nmSiO2_600C1h_0013
TEM image4NM_HEA_5nmSiO2_600C1h_0013.jpg
-
4NM_HEA_5nmSiO2_600C1h_0014
TEM image4NM_HEA_5nmSiO2_600C1h_0014.jpg
-
4NM_HEA_5nmSiO2_600C1h_0015
TEM image4NM_HEA_5nmSiO2_600C1h_0015.jpg
-
4NM_HEA_5nmSiO2_600C1h_0016
TEM image4NM_HEA_5nmSiO2_600C1h_0016.jpg
-
4NM_HEA_5nmSiO2_600C1h_0018
TEM image4NM_HEA_5nmSiO2_600C1h_0018.jpg
-
4NM_HEA_5nmSiO2_600C1h_0019
TEM image4NM_HEA_5nmSiO2_600C1h_0019.jpg
-
4NM_HEA_5nmSiO2_600C1h_0020
TEM image4NM_HEA_5nmSiO2_600C1h_0020.jpg
-
4NM_HEA_5nmSiO2_600C1h_0021
TEM image4NM_HEA_5nmSiO2_600C1h_0021.jpg
-
4NM_HEA_5nmSiO2_600C1h_0022
TEM image4NM_HEA_5nmSiO2_600C1h_0022.jpg
-
4NM_HEA_5nmSiO2_600C1h_0023
TEM image4NM_HEA_5nmSiO2_600C1h_0023.jpg
-
4NM_HEA_5nmSiO2_600C1h_0024
TEM image4NM_HEA_5nmSiO2_600C1h_0024.jpg
-
4NM_HEA_5nmSiO2_600C1h_0025
TEM image4NM_HEA_5nmSiO2_600C1h_0025.jpg
-
4NM_HEA_5nmSiO2_600C1h_0026
TEM image4NM_HEA_5nmSiO2_600C1h_0026.jpg
-
4NM_HEA_5nmSiO2_600C1h_0027
TEM image4NM_HEA_5nmSiO2_600C1h_0027.jpg
-
Map 24NM_HEA_5nmSiO2_600C1h OVERLAY Ag L
Optical microscope image (bmp, jpg)Map 24NM_HEA_5nmSiO2_600C1h OVERLAY Ag L.jpg
-
Map 24NM_HEA_5nmSiO2_600C1h OVERLAY OVERLAY
Optical microscope image (bmp, jpg)Map 24NM_HEA_5nmSiO2_600C1h OVERLAY OVERLAY.jpg
-
Map 24NM_HEA_5nmSiO2_600C1h OVERLAY Pd L
Optical microscope image (bmp, jpg)Map 24NM_HEA_5nmSiO2_600C1h OVERLAY Pd L.jpg
-
Map 24NM_HEA_5nmSiO2_600C1h OVERLAY Si K
Optical microscope image (bmp, jpg)Map 24NM_HEA_5nmSiO2_600C1h OVERLAY Si K.jpg
Referenced Objects (Reverse Association)
-
8433 CRC Ag-Au-Pd-Pt_2
SampleAnnealing at 300°C
-
Interface study with thermal SiO2
Idea or experiment planEffect of having a diffusion barrier to investigate interface and high temperature phase study